S. No |
German
Type |
Sweeden
Type |
EN
Max. |
C
Max. |
Mn.
Max. |
P |
Cr. |
Ni.
Elements |
Mo |
Othar |
200JA |
- |
- |
- |
0.08 |
8.00/9.00 |
0.060 |
15.00/16.00 |
1.00 |
- |
- |
202 J1 |
- |
- |
- |
0.15 |
7.50/10.00 |
0.060 |
16.00/18.00 |
4.00 |
- |
N < 0.25 |
301 |
- |
- |
- |
0.15 |
2.00 |
0.045 |
16.00/18.00 |
6.00/8.00 |
- |
- |
304 |
1.4301 |
2333 |
58E |
0.08 |
2.00 |
0.450 |
18.00/20.00 |
8.00/12.00 |
- |
- |
304L |
1.4306 |
2332 |
- |
0.030 |
2.00 |
0.040 |
18.00/20.00 |
8.00/13.00 |
- |
Ph.0.040 Si0.75 |
309 |
1.4828 |
2352 |
55 |
0.20 |
2.00 |
0.045 |
22.00/24.00 |
12.00/15.00 |
- |
- |
310 |
1.4841 |
2361 |
- |
0.25 |
2.00 |
0.045 |
24.00/26.00 |
19.00/22.00 |
- |
Si 1.50 Max |
316 |
1.4401 |
2343 |
58H |
0.08 |
2.00 |
0.045 |
16.00/18.00 |
10.00/14.00 |
2.00/3.00 |
- |
316L |
1.4404 |
2353 |
58J |
0.030 |
2.00 |
0.040 |
16.00/18.00 |
10.00/15.00 |
2.00/3.00 |
Ph.0.040 Si0.075 |
316Ti |
1.4571 |
2344 |
58J |
0.08 |
2.00 |
- |
16.00/18.00 |
10.00/14.00 |
2.00/3.00 |
- |
317 |
1.4449 |
- |
58J |
0.08 |
2.00 |
0.045 |
18.00/20.00 |
11.00/15.00 |
3.00/4.00 |
- |
317L |
1.4435 |
- |
- |
0.030 |
2.00 |
0.045 |
18.00/20.00 |
11.00/15.00 |
3.00/4.00 |
- |
321 |
1.4541 |
2337 |
58BorC |
0.08 |
2.00 |
0.045 |
17.00/19.00 |
9.00/12.00 |
- |
T:S.YCMin |
347 |
1.4550 |
2338 |
58ForG |
0.08 |
2.00 |
0.045 |
17.00/19.00 |
9.00/13.00 |
- |
Cb-Talo x cMin |
410 |
1.4006 |
2302 |
- |
0.15 |
1.00 |
0.040 |
11.50/13.50 |
- |
- |
- |
410S |
- |
- |
- |
0.08 |
1.00 |
0.040 |
11.50/13.50 |
0.06 Max |
- |
- |
420 |
1.4021 |
2302 |
- |
0.15(min) |
1.00 |
0.040 |
12.00/14.00 |
- |
- |
- |
430 |
1.4016 |
2320 |
- |
0.12 |
1.00 |
0.040 |
16.00/18.00 |
0.75 |
- |
- |
|